Phrozen Aqua 4K 3D Printing Resin
Estimated lead time:2-3 weeks
Estimated lead time for items in restock are calculated from the re-stock time:
Scroll Down for More⬇️
Color:Gray
Size:1 KG
Quantity:
Phrozen Aqua 4K 3D Printer Resin is designed to showcase 3D models in high resolution and works best with the Sonic Mini 4K & Sonic Mighty 4K Resin 3D Printers. With its special formula, Phrozen Aqua 4K 3D Printing Resin creates high-quality & extremely intricate 3D models with 4K resolution.
Benefits
- 【Low Shrinkage & High Precision】 Phrozen Aqua 3D Printing Resins are developed for low shrinkage and high precision printing. Their low warpage & dimensional stability are especially good for precise parts.
- 【Low Viscosity & Low Odor】 Phrozen Aqua3D Printing Resins are easy to print and are easily post-processed due to their low viscosity. Meanwhile, their low odor will not make your place smell.
- 【4K Printing Quality】 Phrozen Aqua 4K Resin is formulated to print with the highest resolution to showcase all the fine details.
- 【Ideal for Miniatures】 With its light color and ultra-high resolution, Aqua-Ivory 4K is perfect as a base color, allowing makers to easily paint and add colors to their detailed designs. With its neutral shade, Aqua-Ivory 4K is ideal for printing out head sculptures, action figure miniatures, and more.
Resources
-
Safety Data Sheet -Download here
- Resin Profile (Click here)
Specs
Phrozen Aqua-Gray 4K
- Weight: 1kg per bottle / 5Kg
- Density: 1.10 g/cm3
- Viscosity: 210-310 cP
- Surface Hardness: 80 Shore D
- UTS: 24 MPa
- Tensile modulus: 1037 MPa
- EAB: 13 %
- Notched Izod Impact:31 J/m
- HDT at 0.45MPa: 70 ℃
Phrozen Aqua-Ivory 4K
- Weight: 1kg per bottle
- Density: 1.10 g/cm3
- Viscosity: 230-330 cP
- Surface Hardness: 80 Shore D
- Tensile Stress at Break: 24 MPa
- Tensile modulus: 1037 MPa
- EAB: 13 %
- Notched Izod Impact:28.80 J/m
- HDT at 0.45MPa: 70 ℃
*All specifications have been tested in a laboratory. Please note that certain specifications may be subject to change without prior notice.